Singlemode Optical Fiber ( 500µm )
This specification conforms to the requirement of IEC 60793 B1.1 and ITU-T G.652.A/B.
|
OPTICAL CHARACTERISTICS
|
|||
|
Characteristics
|
Conditions
|
Specified Values
|
Unit
|
|
Attenuation Coefficient
|
1310 nm
|
≦ 0.34
|
〔dB/km〕
|
|
|
1285 – 1330 nm
|
≦ 0.36
|
〔dB/km〕
|
|
|
1550 nm
|
≦ 0.21
|
〔dB/km〕
|
|
Mode Field Diameter
|
1310 nm
|
8.7 ~ 9.7
|
〔µm〕
|
|
Fiber Cut-Off Wavelength
|
|
1150 ~ 1330
|
〔nm〕
|
|
Cable Cut-Off Wavelength
|
|
< 1260
|
〔nm〕
|
|
Zero Dispersion Wavelength
|
|
1300 ~ 1322
|
〔nm〕
|
|
Zero Dispersion Slope
|
|
≦ 0.092
|
〔ps/(nm2·km)〕
|
|
Dispersion Coefficient
|
1285 – 1330 nm
|
≦ 3.1
|
〔ps/(nm·km)〕
|
|
|
1550 nm
|
≦ 18
|
〔ps/(nm·km)〕
|
|
PMD
|
|
≦ 0.2
|
〔ps/√km〕
|
|
BACKSCATTER CHARACTERISTICS
|
|||
|
Attenuation Directional Uniformity
|
≦ 0.03
|
〔dB/km〕
|
|
|
Attenuation Uniformity
|
|
≦ 0.05
|
〔dB〕
|
|
Reflections
|
|
Not Allowed
|
|
|
Group Index of Refraction
|
1310 nm
|
1.467
|
|
|
|
1550 nm
|
1.468
|
|
|
PHYSICAL CHARACTERISTICS
|
|||
|
Core / Cladding Concentricity Error
|
≦ 0.8
|
〔µm〕
|
|
|
Cladding Diameter
|
|
125 ± 1
|
〔µm〕
|
|
Cladding Non-Circularity
|
|
≦ 2.0
|
〔%〕
|
|
Coating Diameter (UV Curable Acrylate)
|
495 ± 15
|
〔µm〕
|
|
|
Clad/Coat Concentricity Error
|
|
≦ 12
|
〔µm〕
|
|
Fiber curl
|
|
≧ 4
|
〔m〕
|
|
Proof Test
|
|
100
|
〔kpsi〕
|
|
Bend Induced Attenuation at 1625 nm
|
≦ 0.1
|
〔dB〕
|
|
|
(100 turns around a mandrel of 60 mm diameter)
|
|
|
|
|
Fatigue Resistance Parameter (nd)
|
20
|
|
|
|
Coating Strip Force (Typical)
|
130(1.4)
|
〔g〕/ (N)
|
|
|
Length (Typical)
|
|
6.6
|
〔km〕
|
|
ENVIRONMENTAL CHARACTERISTICS
|
|||
|
Temperature Dependence at 1310 nm and 1550 nm
|
≦ 0.05
|
〔dB/km〕
|
|
|
Induced Attenuation – 60°C to +85°C
|
|
|
|
|
Watersoak Dependence at 1310 nm and 1550 nm
|
≦ 0.05
|
〔dB/km〕
|
|
|
Induced Attenuation at 20°C for 30 days
|
|
|
|
|
Damp Heat Dependence at 1310 nm and 1550 nm
|
≦ 0.05
|
〔dB/km〕
|
|
|
Induced Attenuation at 85°C, 85%R.H., 30 days
|
|||